| Formulation Name (Grade: B40E) total : 0 |
|---|
| Formulaton Name (Material: Thermoplastic elastomer > Thermoplastic vulcanizate(TPV)) total : 2 |
|---|
| TPV ; 쇼어 66A |
| TPV ; 쇼어 70A |
| () | B40E (Thermoprene) |  |
화승소재 | |
|---|---|---|---|---|
| Application | 파이프, 호스, 튜브, 생활소비재 > 박스, 기계, 전선피복 > 가스켓, 오링, 씰, 생활소비재 > 용기 뚜껑, 봉합재 (밀봉재), 기계, 전선피복 > 롤, 전자제품 > 사무기기 > 프레임, 생활소비재 > 신발, 자동차 > 내장재 | |||
| Feature | ||||
| Process |
055-383-9201 |
|||
| Mechanical | ||||
|---|---|---|---|---|
| Compression set | 35.0 | % | ASTM D395 | 70℃, 22hr |
| Tensile strength at break | 3.6 | MPa | ASTM D412 | |
| Tear strength | 15000.0 | N/m | ASTM D624 | |
| Shore hardness | 25.0 | ASTM D2240 | ||
| Elongation at break | 450.0 | % | ASTM D412 | |
| Shore hardness | 50.0 | ASTM D2240 | Shore A | |
| Tensile modulus | 1.4 | MPa | ASTM D412 | 100% |
| Physical | ||||
| Melt index | 25.0 | g/10min | ASTM D1238 | |
| Density | 0.95 | g/㎤ | ASTM D1505 | |
| Specific gravity | 0.97 | ASTM D792 | ||
| Vinyl acetate content | 28.0 | wt% | LG method | |
| Thermal | ||||
| Softening temperature | 40.0 | ˚C | ASTM D1525 | |
| Melting temp | 69.0 | ˚C | LG method |