Formulation Name (Grade: 2500N/B) total : 0
Formulaton Name (Material: Thermoplastic elastomer > Thermoplastic vulcanizate(TPV)) total : 2
TPV ; 쇼어 66A
TPV ; 쇼어 70A
() 2500N/B (Innoprene) home 금호폴리켐
  • 열가소성엘라스토머 > Thermoplastic vulcanizate(TPV)
    • Application파이프, 호스, 튜브, 생활소비재 > 박스, 기계, 전선피복 > 롤, 기계, 전선피복 > 가스켓, 오링, 씰, 생활소비재 > 용기 뚜껑, 봉합재 (밀봉재), 전자제품 > 사무기기 > 프레임, 생활소비재 > 신발, 자동차 > 내장재
    Feature
    Process (Call)02-6303-3884
    (Sales)051-514-1564
    jeonghs@polychem.co.kr
    Mechanical
    Izod impact strength(ASTM), Notched 490.3 J/m ASTM D256 23℃
    Compression set 89.0 % ASTM D395 120℃, 70hr
    Compression set 70.0 % ASTM D395 70℃, 22hr
    Tensile strength at yield 31.4 MPa ASTM D638
    Elongation at break 620.0 % ASTM D412
    Flexural modulus 1422.0 MPa ASTM D790
    Shore hardness 48.0 ASTM D2240 Shore D
    Elongation at break Min. 100.0 % ASTM D638
    Tear strength 115640.0 N/m ASTM D624
    Tensile strength at break 2.16 MPa ASTM D412
    Tensile modulus 10.88 MPa ASTM D412 100%
    Izod impact strength(ASTM), Notched 44.1 J/m ASTM D256 -10℃
    Physical
    Density 0.9 g/㎤ ASTM D1505
    Melt index 0.5 g/10min ASTM D1238
    Specific gravity 0.94 ASTM D792
    Thermal
    Heat Deflection Temperature @0.46MPa 125.0 ˚C ASTM D648 0.46MPa
    Flammability
    Flammability HB class UL94
    Other
    Shore hardness after aging 50.0 ASTM D2240 Shore D, 150℃(168hr)
    Tensile strength at break after aging 20.29 MPa ASTM D412 150℃, 168hr
    Fluid resistance-Weight change 0.0 % ASTM D471 50% NaOH, 25℃, 168hr
    Elongation at break after aging 505.0 % ASTM D412 150℃, 168hr
    가스켓, 오링, 씰