| Formulation Name (Grade: 5431B) total : 0 |
|---|
| Formulaton Name (Material: Thermoplastic elastomer > Thermoplastic vulcanizate(TPV)) total : 2 |
|---|
| TPV ; 쇼어 66A |
| TPV ; 쇼어 70A |
| () | 5431B (Innoprene) |  |
금호폴리켐 | |
|---|---|---|---|---|
| Application | 파이프, 호스, 튜브, 자동차 > 내장재, 생활소비재 > 박스, 기계, 전선피복 > 가스켓, 오링, 씰, 생활소비재 > 용기 뚜껑, 봉합재 (밀봉재), 기계, 전선피복 > 롤, 전자제품 > 사무기기 > 프레임, 생활소비재 > 신발 | |||
| Feature | ||||
| Process |
(Call)02-6303-3884 (Sales)051-514-1564 jeonghs@polychem.co.kr |
|||
| Mechanical | ||||
|---|---|---|---|---|
| Flexural modulus | 1373.0 | MPa | ASTM D790 | |
| Izod impact strength(ASTM), Notched | 29.4 | J/m | ASTM D256 | -10℃ |
| Izod impact strength(ASTM), Notched | 78.5 | J/m | ASTM D256 | 23℃ |
| Tensile strength at yield | 27.5 | MPa | ASTM D638 | |
| Elongation at break | Min. 100.0 | % | ASTM D638 | |
| Shore hardness | 40.0 | ISO 868 | Shore D | |
| Elongation at break | 580.0 | % | ISO 37 | |
| Tear strength | 78400.0 | N/m | ISO 34B | |
| Tensile strength at break | 12.05 | MPa | ISO 37 | |
| Tensile modulus | 7.94 | MPa | ISO 37 | 100% |
| Physical | ||||
| Melt index | 6.0 | g/10min | ASTM D1238 | |
| Density | 0.9 | g/㎤ | ASTM D1505 | |
| Specific gravity | 0.89 | ISO 1183 | ||
| Thermal | ||||
| Heat Deflection Temperature @0.46MPa | 120.0 | ˚C | ASTM D648 | 0.46MPa |
| Flammability | ||||
| Flammability | HB | class | UL94 | |
| Other | ||||
| Elongation at break after aging | 512.0 | % | ISO 188 | 80℃, 70hr |
| Modulus after aging | 9.11 | MPa | ISO 188 | 80℃, 70hr |
| Shore hardness after aging | 38.0 | ISO 188 | Shore D, 80℃(70hr) | |
| Tensile strength at break after aging | 10.68 | MPa | ISO 188 | 80℃, 70hr |
| 가스켓, 오링, 씰 | |||
| Region | Update | 2016.07.21 | |