Formulation Name (Grade: 1640N/B) total : 0
Formulaton Name (Material: Thermoplastic elastomer > Thermoplastic vulcanizate(TPV)) total : 2
TPV ; 쇼어 66A
TPV ; 쇼어 70A
() 1640N/B (Innoprene) home 금호폴리켐
  • 열가소성엘라스토머 > Thermoplastic vulcanizate(TPV)
    • Application파이프, 호스, 튜브, 기계, 전선피복 > 가스켓, 오링, 씰, 생활소비재 > 용기 뚜껑, 봉합재 (밀봉재), 기계, 전선피복 > 롤, 전자제품 > 사무기기 > 프레임, 생활소비재 > 신발, 자동차 > 내장재, 생활소비재 > 박스
    Feature
    Process (Call)02-6303-3884
    (Sales)051-514-1564
    jeonghs@polychem.co.kr
    Mechanical
    Flexural modulus 1127.8 MPa ASTM D790
    Izod impact strength(ASTM), Notched 34.3 J/m ASTM D256 23℃
    Tensile modulus 2.35 MPa ASTM D412 100%
    Elongation at break Min. 100.0 % ASTM D638
    Izod impact strength(ASTM), Notched 24.5 J/m ASTM D256 -10℃
    Tear strength 34300.0 N/m ASTM D624
    Rockwell hardness 95.0 ASTM D785 R scale
    Shore hardness 65.0 ASTM D2240 Shore A
    Compression set 45.0 % ASTM D395 120℃, 70hr
    Tensile strength at break 6.86 MPa ASTM D412
    Tensile strength at yield 27.5 MPa ASTM D638
    Elongation at break 604.0 % ASTM D412
    Compression set 35.0 % ASTM D395 70℃, 22hr
    Physical
    Density 0.9 g/㎤ ASTM D1505
    Specific gravity 0.95 ASTM D792
    Melt index 44.0 g/10min ASTM D1238
    Thermal
    Heat Deflection Temperature @0.46MPa 95.0 ˚C ASTM D648 0.46MPa
    Optical
    Haze 25.0 % ASTM D1003
    Other
    Shore hardness after aging 67.0 ASTM D2240 Shore A, 150℃(168hr)
    Tensile strength at break after aging 6.17 MPa ASTM D412 150℃, 168hr
    Fluid resistance-Weight change 0.0 % ASTM D471 50% NaOH, 25℃, 168hr
    Elongation at break after aging 530.0 % ASTM D412 150℃, 168hr
    Fluid resistance-Weight change 2.0 % ASTM D471 50% NaOH, 25℃, 168hr
    가스켓, 오링, 씰