Formulation Name (Grade: 1730N/B) total : 0
Formulaton Name (Material: Thermoplastic elastomer > Thermoplastic vulcanizate(TPV)) total : 2
TPV ; 쇼어 66A
TPV ; 쇼어 70A
() 1730N/B (Innoprene) home 금호폴리켐
  • 열가소성엘라스토머 > Thermoplastic vulcanizate(TPV)
    • Application파이프, 호스, 튜브, 생활소비재 > 박스, 기계, 전선피복 > 가스켓, 오링, 씰, 생활소비재 > 용기 뚜껑, 봉합재 (밀봉재), 기계, 전선피복 > 롤, 전자제품 > 사무기기 > 프레임, 생활소비재 > 신발, 자동차 > 내장재
    Feature
    Process (Call)02-6303-3884
    (Sales)051-514-1564
    jeonghs@polychem.co.kr
    Mechanical
    Tear strength 42100.0 N/m ASTM D624
    Compression set 39.0 % ASTM D395 70℃, 22hr
    Tensile strength at break 8.13 MPa ASTM D412
    Tensile modulus 2.64 MPa ASTM D412 100%
    Compression set 55.0 % ASTM D395 120℃, 70hr
    Elongation at break 595.0 % ASTM D412
    Shore hardness 75.0 ASTM D2240 Shore A
    Physical
    Density 1.39 ~ 1.41 g/㎤ ASTM D1505
    Specific gravity 0.96 ASTM D792
    Intrinsic viscosity [eta] 0.82 ~ 0.86 dl/g ASTM D4603
    Acetaldehyde content Max. 1.0 ppm WI-QS-S06
    Thermal
    Melting temp 242.0 ~ 248.0 ˚C ASTM D3418
    Other
    Shore hardness after aging 76.0 ASTM D2240 Shore A, 150℃(168hr)
    Elongation at break after aging 460.0 % ASTM D412 150℃, 168hr
    Fluid resistance-Weight change 0.0 % ASTM D471 50% NaOH, 25℃, 168hr
    Tensile strength at break after aging 6.66 MPa ASTM D412 150℃, 168hr
    Fluid resistance-Weight change 3.0 % ASTM D471 50% NaOH, 25℃, 168hr
    Chip size 1.3 ~ 1.7 g/100ea WI-QS-S05
    가스켓, 오링, 씰