Formulation Name (Grade: 1800N/B) total : 0
Formulaton Name (Material: Thermoplastic elastomer > Thermoplastic vulcanizate(TPV): 10% GF) total : 0
() 1800N/B (Innoprene) home 금호폴리켐
  • 열가소성엘라스토머 > Thermoplastic vulcanizate(TPV): 10% GF
    • Application파이프, 호스, 튜브, 자동차 > 내장재, 생활소비재 > 박스, 기계, 전선피복 > 가스켓, 오링, 씰, 생활소비재 > 용기 뚜껑, 봉합재 (밀봉재), 기계, 전선피복 > 롤, 전자제품 > 사무기기 > 프레임, 생활소비재 > 신발
    Feature
    Process (Call)02-6303-3884
    (Sales)051-514-1564
    jeonghs@polychem.co.kr
    Mechanical
    Tensile strength at break 10.88 MPa ASTM D412
    Izod impact strength(ASTM), Notched 98.1 J/m ASTM D256 23℃, 1/8inch
    Tensile strength at yield 93.2 MPa ASTM D638 50mmmin
    Tear strength 49000.0 N/m ASTM D624
    Flexural modulus 5295.7 MPa ASTM D790 10mmmin
    Elongation at break Min. 4.0 % ASTM D638 50mmmin
    Shore hardness 80.0 ASTM D2240 Shore A
    Compression set 60.0 % ASTM D395 120℃, 70hr
    Compression set 45.0 % ASTM D395 70℃, 22hr
    Flexural strength at break 137.3 MPa ASTM D790 10mmmin
    Elongation at break 614.0 % ASTM D412
    Tensile modulus 3.53 MPa ASTM D412 100%
    Physical
    Specific gravity 0.96 ASTM D792
    Specific gravity 1.3 ASTM D792
    Thermal
    Heat Deflection Temperature @1.82MPa 120.0 ˚C ASTM D648 1.82MPa
    Flammability
    Flammability V-0 class UL94 1.5mm
    Other
    Tensile strength at break after aging 7.94 MPa ASTM D412 150℃, 168hr
    Elongation at break after aging 420.0 % ASTM D412 150℃, 168hr
    Fluid resistance-Weight change 0.0 % ASTM D471 50% NaOH, 25℃, 168hr
    Fluid resistance-Weight change 2.0 % ASTM D471 50% NaOH, 25℃, 168hr
    Shore hardness after aging 85.0 ASTM D2240 Shore A, 150℃(168hr)
    Mold shrinkage 0.1 ~ 0.3 % ASTM D955